Solution: preheat before welding to reduce the impact of long-term oil immersion until all the oil stains inside the organization are volatilized and burned at a high temperature.
Solution: the welding rod needs to be preheated and used after being dried in a drying cylinder.
Solution: the quality of the cast iron electrode itself needs to be professionally controlled and selected. Cast iron electrodes with better quality can be selected.
Solution: only through welding to produce pores, then grinding, and then overlapping the previous welding spot for welding, this treatment is slow, but the effect is also the best.
It is generally believed that under the rapid cooling condition of 30-100 ℃ /s, the carbon melted in iron does not have time to precipitate in the form of graphite, but appears as cementite, that is, the so-called white mouth. The white structure is hard and brittle, which makes the weld difficult for the machine after welding, and even leads to cracking.
Preventive measures:
Preheating before welding and heat preservation after welding; Properly adjust the chemical composition and cooling rate of filler metal; Improve the chemical composition of weld metal.
Because the plasticity of gray cast iron is extremely poor, almost no plastic deformation can occur, and the strength is low, so under the joint action of welding stress and casting stress (structural stress), when the local stress is greater than the strength limit, cracks will occur.
Preventive measures:
Using arc cold welding to reduce welding stress
Select welding materials with good plasticities, such as nickel, copper, nickel copper, high vanadium steel, etc. as filler metal, so that the weld metal can relax the stress through plastic deformation and prevent cracks; Stress can be eliminated by hammering the weld to prevent cracks; When the weld is cooled, it can make up the hindered bottom to contract freely, to avoid cracks caused by excessive force.
Adopt the thermal welding method and control the temperature
When the temperature is higher than 600 ℃, due to certain plastic deformation Some internal stresses are eliminated, and thermal stress cracks will not occur when welding above 600 ℃.